IPALEN 1000® (UHMW-PE)
anti-adhesive bunker lining
 |
|
|
|
|
|
 |
|
||||
 |
|
||||
 |
|
||||
 |
|
||||
 |
|
||||
 |
|
||||
 |
|
||||
 |
|
||||
 |
|
||||
 |
|
||||
 |
 |
 |
 |
 |
|
 |
 |
|
|||
Technical specifications
|
Units |
|
Density |
|
0,936 |
Linear expansion coefficient between +20° C and 100° C |
|
2,10 -4 |
Tensile strength |
|
|
at 23° C |
N/mm² |
22 |
àat 120° C |
N/mm² |
3,6 |
Breaking strength |
|
|
at 23° C |
N/mm² |
44 |
at 120° C |
N/mm² |
23 |
Elongation at break |
|
|
at 23° C |
% |
450 |
at 120° C |
% |
900 |
Impact strength on a notched test bar |
mJ/mm² |
140/180 |
Ball indentation hardness (365 N) |
N/mm² |
40 |
Friction coefficient on straightened steel |
|
|
Ra = 1,6 – pressure 41 kg/cm² |
|
0,15 |
Abrasion resistance |
Base 100 * |
100 |
Surface resistivity |
0hm |
> 10 13 |
Volume resistivity |
0hm.cm |
> 5.10 6 |
* the baseline figure of 100 corresponds to the weight of the material lifted off after use of an abrasive disk on a block of standard quality IPALEN1000 during a specific test of this material. For other categories of material, a high value signifies that the material is less
resistant to abrasion as the weight of matter lifted off under the same testing
conditions is superior. Inversely, a lower value signifies that the material displays
greater resistance to abrasion.
![[voir la suite]](../../../img/com/arrow_right.gif){kind=icon}